Abstract
GaAs/Al x Ga (1−x) As quantum well lasers have been demonstrated via organometallic chemical vapor deposition on relaxed graded Ge/GexSi(1−x) virtual substrates on Si. A number of GaAs/Ge/Si integration issues including Ge autodoping behavior in GaAs, reduced critical thickness due to thermal expansion mismatch, and complications with mirror facet cleaving have been overcome. Despite unoptimized laser structures with high series resistance and large threshold current densities, surface threading dislocation densities for GaAs/AlGaAs lasers on Si substrates as low as 2×106 cm−2 permitted continuous room-temperature lasing at a wavelength of 858 nm. The laser structures are uncoated edge-emitting broad-area devices with differential quantum efficiencies of 0.24 and threshold current densities of 577 A/cm2. Identical devices grown on commercial GaAs substrates showed similar behavior. This comparative data agrees with previous measurements of near-bulk minority carrier lifetimes in GaAs grown on Ge/GeSi/Si substrates.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.