Abstract
Molybdenum as a potentially new biodegradable material was investigated. Degradation behavior of commercially high purity molybdenum was observed in simulated physiological salt solutions (Kokubo's SBF with/without TRIS-HCl, Cu2+ addition and 0.9 % NaCl solution). Potentiodynamic polarization, immersion mass loss and ion concentration measurements paired with REM/EDX analysis reveal gradual dissolution of molybdenum in the proper order of magnitude for stent application, associated with formation of thin, non-passivating corrosion products. The underlying corrosion mechanism is discussed as well as a comparison to literature data. However, formation of calcium phosphates (CaP) in SBF significantly decreases corrosion rates. In-situ polarization was found to be a potential way for overcoming this problem and simultaneously enhancing corrosion above the benchmark for a degradable stent material. A first in-vitro cytotoxicity assessment for HFIB fibroblasts in direct contact to corroding molybdenum did not show any signs for decreased cell viability. Thus, molybdenum appears to be a promising novel biodegradable metal for structural applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.