Abstract
To investigate the facile conversion of biomass wastes into carbon-based adsorbents with efficient carbon capture, porous hierarchical biochar was novelly fabricated by molten salt-assisted pyrolysis under different inducing atmospheres (air and nitrogen) and temperatures. The pyrolysis characteristics of biomass waste in molten salt (K2CO3-Na2CO3-Li2CO3) were probed by a thermogravimetric analyzer-differential scanning calorimeter (TG-DSC). Further, the physicochemical properties of biochar, recovery of molten salt, and CO2 adsorption performance were investigated comprehensively. The molten salt biochar had a high specific surface area (324.21–788.81 m2 g−1). The biochar prepared in the air had a better CO2 adsorption capacity of up to 72.42 mg g−1, which was 20 % higher than the CO2 adsorption capacity of the biochar prepared in a nitrogen atmosphere. In addition, the recovery of molten salt was higher in the air-induced atmosphere. At an induction temperature of 900 °C, the recovery ratio of potassium in the air atmosphere was twice as high as that in nitrogen. Meanwhile, the potassium and sodium contents embedded in the biochar were lower in the air atmosphere. The pathway presented here will provide a novel and simple approach for the large-scale preparation of carbon-based adsorbents from biomass waste.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.