Abstract
The hexagonal plate-like single crystals of a new compound PrRh4.8B2 were obtained by a molten metal flux growth method using Cu as a flux. PrRh4.8B2 is orthorhombic with the space group Fmmm; a=0.9697(4) nm, b=0.5577(2) nm and c=2.564(3)nm. The structure of the compound is of a modified CeCo3B2-type which is explained by a stacking model of Pr–B and rhodium layers. The temperature dependence of inverse static magnetic susceptibility, χ−1 obeys the Curie–Weiss law at higher temperature above 50 K. The μeff is 4.2 μB and Θp is −13 K. The value of the observed effective magnetic moment is larger than the value of 3.6 μB for the free trivalent ion Pr3+. The susceptibility deviates from the Curie–Weiss law, below 50 K, suggesting some magnetic ordering. The value of MVH for c-plane with the orthorhombic symmetry of PrRh4.8B2 is 6.7±0.6 GPa. The TG curve represents that oxidation of the PrRh4.8B2 proceeds above 600°C. Weight gain of the specimen heated up to 1200°C in air is 13%. After TG–DTA measurement, final product is PrBO3 and Rh.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.