Molecularly Smooth Single-Crystalline Films of Thiophene–Phenylene Co-Oligomers Grown at the Gas–Liquid Interface

Abstract

Single crystals of thiophene–phenelyne co-oligomers (TPCOs) have previously shown their potential for organic optoelectronics. Here we report on solution growth of large-area thin single-crystalline films of TPCOs at the gas–liquid interface by using solvent–antisolvent crystallization, isothermal slow solvent evaporation, and isochoric cooling. The studied co-oligomers contain identical conjugated core (5,5′-diphyenyl-2,2′-bithiophene) and different terminal substituents, fluorine, trimethylsilyl, or trifluoromethyl. The fabricated films are molecularly smooth over areas larger than 10 × 10 μm2, which is of high importance for organic field-effect devices. The low-defect structure of the TPCO crystals is suggested from the monoexponential kinetics of the PL decay measured in a wide dynamic range (up to four decades) and from low crystal mosaicity assessed by microfocus X-ray diffraction. The TPCO crystal structure is solved using a combination of X-ray and electron diffraction. The terminal substituents affect the crystal structure of TPCOs, bringing about the formation of a noncentrosymmetric crystal lattice with a crystal symmetry Cc for the bulkiest trimethylsilyl terminal groups, which is unusual for linear conjugated oligomers. Comparing the different crystal growth techniques, it is concluded that the solvent–antisolvent crystallization is the most robust for fabrication of single-crystalline TPCOs films. The possible nucleation and crystallization mechanisms operating at the gas–solution interface are discussed.