Abstract
Nano-MgO thin films were grown on the cleaned glass substrate via sol-gel spin coating techniques using magnesium acetate tetrahydrate, ethanol and nitric acid. For the thin films deposition, the solutions were prepared at six different molar concentrations (0.1M, 0.2M, 0.4M, 0.6M, 0.8M and 1M). The thickness and roughness of nano-MgO films was found to be increased with an increase of molar concentration. The increment in particle size and agglomerated particles were observed from FESEM (JEOL JSM-J600F) images as the molar concentration increased from 0.1M to 1.0M. The results showed 0.4M nano-MgO films have the best properties for example it has a uniform film, non-porous structure and has nanometer dimension size which around 42.8nm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.