Modulation of magnetic coercivity in Ni thin films by reversible control of strain

Abstract

In this study, we demonstrated the magnetoelectric control of magnetic thin films . (111)-textured Pd/Ni/Pd thin films were prepared on mica/lead zirconium titanate (PZT) substrates for the investigation. The reversible modulation of magnetic coercivity in Ni films was observed through the electric-voltage-controlled strain variation from the PZT substrate. For 14 nm Ni film, the applied electric field of ±350 V/m led to ±0.5% strain variation of PZT, which was transferred to ±0.4% strain variation of Pd/Ni/Pd thin films on mica, and resulted in ∓17 Oe (∓5% of the preliminary magnetic coercivity). The reversible modulation of magnetic coercivity is supposed to be caused by the voltage-controlled strain through the magneto-elastic effect. • The magnetoelectric control of the magnetic coercivity of Pd/Ni/Pd thin films was demonstrated. • The ±0.4% strain variation of 14 nm Ni thin films resulted in ±17 Oe change of H c . • The reversible modulation of H c is supposed to be caused by the magneto-elastic effect.