A series of flower-like magnesium silicate samples with hierarchical pore were prepared by the solvothermal method under template-free conditions using sodium dodecyl sulfate as the modifier and ethanol-water as the solvent. These samples were characterized by various methods and were evaluated for the adsorption of heavy metal Cd2+. The results showed that the adding modifier did not change the crystal structure of the magnesium silicate samples. In the range of 2~80 nm, they still showed hierarchical pore distribution mainly composed of mesopores and macropores, which facilitates the rapid transport of adsorbent within the pore channel. Therefore, the adsorption of Cd2+ was greatly accelerated. Meanwhile, the larger specific surface area (as high as 553 m2/g) of these samples significantly increased the theoretical maximum adsorption amount of Cd2+ up to 295.3 mg/g due to more available adsorption sites. The adsorption dynamic behavior of the samples on Cd2+ was in accordance with the pseudo-second-order adsorption model, and their thermodynamic behavior follows the Langmuir adsorption model. The adsorption mechanism of the sample was proposed as electrostatic adsorption and exchange of metal ions and acidic groups on its surface with ions in solution. The obtained magnesium silicate materials are expected to remove heavy metals from wastewater.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Environmental science and pollution research international
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.