Abstract
Nd2-xNi0.75Cu0.2M0.05O4±δ (x = 0 and 0.1; M = Sc, Ga, and In) Ruddlesden-Popper-type oxides are obtained by a sol-gel route and characterized concerning phase composition and crystal structure. It is found that the largest In3+ cannot be effectively introduced into the structure, while Nd stoichiometric and cation-deficient Nd2-xNi0.75Cu0.2Sc0.05O4±δ and Nd2-xNi0.75Cu0.2Ga0.05O4±δ (x = 0; 0.1) can be obtained as single-phase materials. Systematic characterization of the crystal structure at high temperatures, oxygen content, as well as transport properties reveals that while the Nd-site deficiency has rather negligible influence on the structure, it causes a substantial decrease of the oxygen content, which at high temperatures leads to a change of the dominant type of defects from the oxygen interstitials to the vacancies for Nd1.9Ni0.75Cu0.2Sc0.05O4±δ and Nd1.9Ni0.75Cu0.2Ga0.05O4±δ. The Nd-site deficiency also causes a decrease of the total conductivity. Importantly, all the examined materials exhibit full chemical stability in CO2 atmosphere, which together with moderate thermal expansion makes them good candidates for the oxygen transport membranes, which can be used e.g. in the air separation technologies. The selected Sc- and Ga-doped compounds evaluated as ceramic membranes show relatively high oxygen fluxes, with the highest value of 0.78 mL cm-2 min-1 at ca. 880 °C registered for 0.9 mm thick, dense Nd1.9Ni0.75Cu0.2Ga0.05O4±δ membrane.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.