Abstract
Nano crystalline tin oxide thin films were deposited on Si and quartz substrates using R. F. magnetron sputtering technique. A set of films was annealed in oxygen environment. These as-deposited and annealed films were irradiated using 100 MeV Ag ions at different fluences ranging from 3×10 11 to 3×10 13 ions/cm 2 . The structural, optical and surface morphological properties of films were studied using X-ray diffraction (XRD), UV-Vis spectroscopy, and atomic force microscopy (AFM) techniques. As deposited films showed the polycrystalline nature and annealing enhances the crystallinity along a particular plane. Upon irradiation at lower fluences up to 3×10 12 ions/cm 2 , reduction in crystallinity is observed but at highest fluence 1×10 13 ions/cm 2 a small increase in crystallinity occurs as inferred from XRD spectra. UV-Vis study showed red shift at the lower fluences and blue shift at higher fluences. The pristine film, as observed in AFM micrograph, has randomly distributed surface nano structures with broader size distribution. Irradiation induces the formation of regular shape structures with narrow size distribution. These results may be attributed to the energy deposited by swift heavy ions in the film. Copyright © 2013 VBRI press.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.