Abstract
This study aims to analyze the effects of supercritical carbonation (CO2 at 20 MPa and 318 K) on the physicochemical properties of ordinary Portland cement pastes. The evolution of the main crystalline phases of the cement pastes during carbonation was determined by means of X-ray diffraction and thermogravimetric analysis. The pore structure was analyzed by low-temperature N2 adsorption−desorption and mercury intrusion porosimetry techniques. Finally, the microstructure of the samples was observed by using scanning electron microscopy coupled with energy-dispersive X-ray detection for chemical analysis. For a natural carbonation process, diffusion of CO2 into the pores of the cement paste is considered as the rate-controlling step. Instead, the accelerated reaction kinetics of calcium carbonate precipitation in the supercritical process was chemically controlled by the detachment of calcium ions from solid portlandite or CSH gel. The total pore volume of the studied cement pastes decreased with carbonation, which was associated with the deposition of the formed CaCO3. Samples carbonated under the supercritical conditions developed a higher volume of gel pores than those obtained by natural carbonation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.