Abstract
Silica-based resistive random access memory devices have become an active research area due to complementary metal-oxide-semiconductor compatibility and recent dramatic increases in their performance and endurance. In spite of both experimental and theoretical insights gained into the electroforming process, many atomistic aspects of the set and reset operation of these devices are still poorly understood. Recently a mechanism of electroforming process based on the formation of neutral oxygen vacancies (VO0) and interstitial O ions (Oi2-) facilitated by electron injection into the oxide has been proposed. In this work, we extend the description of the bulk (Oi2-) migration to the interface of amorphous SiO2 with the polycrystaline TiN electrode, using density functional theory simulations. The results demonstrate a strong kinetic and thermodynamic drive for the movement of Oi2- to the interface, with dramatically reduced incorporation energies and migration barriers close to the interface. The arrival of Oi2- at the interface is accompanied by preferential oxidation of undercoordinated Ti sites at the interface, forming a Ti-O layer. We investigate how O ions incorporate into a perfect and defective ∑5(012)[100] grain boundary (GB) in TiN oriented perpendicular to the interface. Our simulations demonstrate the preferential incorporation of Oi at defects within the TiN GB and their fast diffusion along a passivated grain boundary. They explain how, as a result of electroforming, the system undergoes very significant structural changes with the oxide being significantly reduced, interface being oxidized, and part of the oxygen leaving the system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.