Modeling of beryllium sputtering and re-deposition in fusion reactor plasma facing components

Abstract

Quantitative characteristics of Be-sputtering by hydrogen isotope ions in a magnetron sputtering system, the microstructure and composition of the sputtered and re-deposited layers were studied. The energies of H + and D + ions varied from 200 to 300 eV. The ion flux density was ∼3 × 10 21 m −2 s −1. The irradiation doses were up to 4 × 10 25 m −2. For modeling of the sputtered Be-atom re-deposition at increased deuterium pressures (up to 0.07 torr), a mode of operation with their effective return to the Be-target surface was implemented. An atomic ratio O/Be ≅ 0.8 was measured in the re-deposited layers. A ratio D/Be decreases from 0.15 at 375 K to 0.05 at 575 K and slightly grows in the presence of carbon and tungsten. The oxygen concentration in the sputtered layers does not exceed 3 at.%. The atomic ratio D/Be decreases there from 0.07 to 0.03 at target temperatures increase from 350 to 420 K.