Abstract
Record-high electron mobilities were achieved for silicon-doped (010) β-Ga2O3 homoepitaxial films grown via metalorganic chemical vapor deposition (MOCVD). Key growth parameters were investigated to reduce the background doping and compensation concentration. Controllable n-type Si doping was achieved as low as low-1016 cm−3. Record carrier mobilities of 184 cm2/V s at room temperature and 4984 cm2/V s at low temperature (45 K) were measured for β-Ga2O3 thin films with room-temperature doping concentrations of 2.5 × 1016 and 2.75 × 1016 cm−3, respectively. Analysis of temperature-dependent Hall mobility and carrier concentration data revealed a low compensation concentration of 9.4 × 1014 cm−3. Using the two-donor model, Si on the tetrahedrally coordinated Ga(I) site represented the primary shallow donor state, and the secondary donor state was found to possess an activation energy of 120 meV. The demonstration of high-purity and high-quality β-Ga2O3 thin films with uniform and smooth surface morphology via MOCVD will harness its advantages as an ultrawide-bandgap semiconductor for power electronic and short-wavelength optoelectronic device applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.