Abstract
Mo5SiB2-based ceramics were fabricated from elemental powders by forced SHS compaction and hot pressing of SHS-produced powders and specific features of product patterning were characterized by XRD, time-resolved XRD, SEM/EDS, and TEM/EDS. Best results were obtained upon hot pressing of SHS-produced Mo–Si–B powders: resultant material was single-phased Mo5SiB2 with a mean grain size of 2–10 μm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Self-Propagating High-Temperature Synthesis
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.