Abstract
Reduction of La(1-x)Ca(x)MnO(3) (0.6 ≤ x ≤ 1) perovskite phases with sodium hydride yields materials of composition La(1-x)Ca(x)MnO(2+δ). The calcium-rich phases (x = 0.9, 1) adopt (La(0.9)Ca(0.1))(0.5)Mn(0.5)O disordered rocksalt structures. However local structure analysis using reverse Monte Carlo refinement of models against pair distribution functions obtained from neutron total scattering data reveals lanthanum-rich La(1-x)Ca(x)MnO(2+δ) (x = 0.6, 0.67, 0.7) phases adopt disordered structures consisting of an intergrowth of sheets of MnO(6) octahedra and sheets of MnO(4) tetrahedra. X-ray absorption data confirm the presence of Mn(I) centers in La(1-x)Ca(x)MnO(2+δ) phases with x < 1. Low-temperature neutron diffraction data reveal La(1-x)Ca(x)MnO(2+δ) (x = 0.6, 0.67, 0.7) phases become antiferromagnetically ordered at low temperature.