Abstract
The mixing of Au in Si induced by secondary and high-order recoil implantation was investigated using 350 keV Ar+ and 350 keV Kr+ ions to fluences from 1 × 1016 to 3 × 1016 ions/cm2 at room temperature. The thickness of the Au layer evaporated on Si substrate was ∼2400 Å.The ranges of the Ar and Kr ions were chosen to be lower than the thickness of the Au layer in order to avoid the ballistic mixing produced by the primary knock-on atoms. Rutherford backscattering spectrometry (RBS) experiments were carried out to study the effects induced by Ar and Kr irradiation at the interface of Au–Si system. We observed that in the case of the irradiation with Ar+ ions, a broadening of the Au–Si interface occurred only at the fluence of 3 × 1016 Ar+/cm2 and it is attributed to the surface roughening induced by ion bombardment. In contrast, the RBS analysis of a sample irradiated with 2 × 1016 Kr+/cm2 clearly showed, in addition to the broadening effect, the formation of a mixed zone of Au and Si atoms at the interface. The mixing of Au in Si atoms can be explained by the secondary and high-order recoil implantation followed by subsequent collision cascades.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.