Abstract
Static diametrical compression tests conducted on inclined cracked chevron notched Brazilian disc (CCNBD) Brisbane tuff specimens showed that the notched cracks at the centre of the specimens opened (Mode I) up to 30° crack inclination angle (β), whereas crack closure (Mode II) started for β > 33°, and closure became more pronounced at even higher β of 45° and 70°. Both the experimental and numerical results showed that the crack initiation angle (θ) was a function of the β. Scanning electron microscope (SEM) images showed that fatigue damage on cyclic loading of Brisbane tuff is strongly influenced by the failure of the matrix due to both intergranular and transgranular fracturing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.