An Al single crystal with the axial direction of (452) was fatigued in air, at a constant resolved shear stress amplitude (4 MPa), a frequency of 20 Hz and at room temperature. Time-resolved measurements were then carried out on short cracks in persistent slip bands (PSBS) on the top surface, which has the largest slip steps, using the acoustic signal from the crack, when the acoustic lens was scanned over the crack sending convergent acoustic beams down the specimen, was detected and interpreted quantitatively. The signal results from the reflections of a mixed mode surface wave (Rayleigh longitudinal lateral wave) from the crack mouth. At 1.2*106 cycles, two short cracks in the PSB were measured to be 17 and 27 mu m in depth. The angle with the specimen surface was observed to be about 54 degrees , compared with a value of 51 degrees determined by an X-ray method.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.