Abstract
The miscibility, crystallization behaviors, and morphology of polyamide 56/polyamide 6 (PA56/PA6) blends were investigated. The blends had only one Tg, which confirmed that PA56 and PA6 are miscible in the blends. The melting point, crystallization temperature, crystallinity of the blends depressed due to the interaction of PA56 and PA6 in the blends. The crystalline structure of both PA56 and PA6 in the blends did not change and crystallized separately in both isothermal and non-isothermal crystallization process. PA56 in the blends crystallized in all blending ratio, while PA6 only crystallized with PA6 content φ6 > 0.2. The crystals of PA56 and PA6 grew in the same crystal skeleton but in different layers. Mechanical properties of the blends indicated that the elongation at break could be improved significantly without scarifying the strength in the case of adding a small amount of PA6 in PA56, which provides a promising approach for fabricating polyamide materials with desired properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.