Abstract
The migration study of nano-Ag migration from polylactic acid (PLA) films was studied. Samples treated by high-pressure food processing (0, 100, 200, 300, and 400MPa pressure) were soaked in acetic acid solution and incubated at 20°C for 90 days. At the end of storage, nano-Ag particles (AgNPs) migration from the PLA/AgNPs composite film treated under 200MPa high pressure was the lowest. However, AgNPs migration was accelerated under 400MPa high pressure. High-pressure processing (200MPa) could cause denser structure and higher crystallinity degree in films than other treatments. Lower amount of AgNPs induced a decline in the intensity of specific characteristic peaks. The diffraction peak intensity of α-crystal for the film sample treated with 400MPa was the lowest on day 60. The crystallization index of the PLA matrix changed with different high-pressure processing. The result indicated that appropriate high-pressure food processing could effectively suppress AgNPs migration from PLA-based film while contacting with acidic acid food simulant. PRACTICAL APPLICATION: The release of nanoparticles from food packaging material is a very important matter when the migration is concerned with regulatory and toxicity issues. The study described the migration kinetic of AgNPs from PLA nanocomposite film into acidic food simulant after different high-pressure food processing. The results indicated that the PLA/AgNPs nanocomposite film was safe for acidic food after high-pressure treatment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.