Abstract
Zn,Al–CO 3 compounds with the hydrotalcite-like (layered double hydroxide, LDH) structure were prepared by a co-precipitation method followed by hydrothermal treatment under microwave irradiation. The influence of the ageing treatment was studied in two series of samples with different Zn 2+/Al 3+ ratios, namely, 3/1 and 2/1. Moreover, the effects of the heating temperature and of the irradiation time were studied in order to select the optimum preparation conditions. The solids were fully characterised by powder X-ray diffraction (PXRD), 27Al MAS-NMR, FT-IR spectroscopy, thermal analyses (DTA and TG), N 2 adsorption/desorption at −196 °C and TEM. The results showed that whatever the chemical composition of the starting mixture, HTlcs with Zn 2+/Al 3+ ratio equal to 2 were obtained, and it was impossible to overcome the ZnO segregation when the molar ratio was >2. These compounds were stable and their crystallinity could be quickly enhanced when the temperature treatment was 100 °C, whereas at 125 °C the ZnO segregation was not prevented.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.