Microwave‐assisted rapid polycondensation reaction of 4‐(4′‐acetamidophenyl)‐1,2,4‐triazolidine‐3,5‐dione with diisocyanates

Abstract

Abstract4‐(4′‐Aminophenyl)‐1,2,4‐triazolidine‐3,5‐dione was reacted with 1 mol of acetyl chloride in dry N,N‐dimethylacetamide (DMAc) at −15°C and 4‐(4′‐acetamidophenyl)‐1,2,4‐triazolidine‐3,5‐dione [4‐(4′‐acetanilido)‐1,2,4‐triazolidine‐3,5‐dione] (APTD) was obtained in high yield. The reaction of the APTD monomer with excess n‐isopropylisocyanate was performed at room temperature in DMAc solution. The resulting bis‐urea derivative was obtained in high yield and was finally used as a model for the polymerization reaction. The step‐growth polymerization reactions of monomer APTD with hexamethylene diisocyanate, isophorone diisocyanate, and tolylene‐2,4‐diisocyanate were performed under microwave irradiation and solution polymerization in the presence of pyridine, triethylamine, or dibutyltin dilaurate as a catalyst. Polycondensation proceeded rapidly, compared with conventional solution polycondensation; it was almost completed within 8 min. The resulting novel polyureas had an inherent viscosity in the range of 0.07–0.17 dL/g in dimethylformamide or sulfuric acid at 25°C. These polyureas were characterized by IR, 1H‐NMR, elemental analysis, and thermogravimetric analysis. The physical properties and structural characterization of these novel polyureas are reported. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 2103–2113, 2004