Abstract
The ferrous removal process after carbothermic reduction of chromite fines with microwave heating combined with leaching was investigated. Under the following conditions: Reaction temperature: 1150°C , Reaction time : 40min, Semi coke ratio: 12% , the iron content of the reduction product : 13.05% . Metallization achieved was 52.7%. Reduced chromite was leached with 8% of H2SO4 and FeCl3 aqueous solution. The results show that: the recovery rate of chromium can reach 88.06%, the mass ratio of chromium to iron is 3.5:1 for leaching 30 minutes with 8% of H2SO4; the recovery rate of chromium can reach 88.91%, the mass ratio of chromium and iron is 2.56:1 for leaching 4h at room temperature with FeCl3 aqueous solution (100g/L). The leaching time of latter is longer but can realize the circulation effectively and reduce the waste liquid processing problem.1
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.