Abstract
High-quality thin films of YBa/sub 2/Cu/sub 3/O/sub 7- delta / have been deposited by metalorganic chemical vapor deposition on both sides of 15-mm*15-mm <100> LaAlO/sub 3/ substrates without requiring the use of heat-sinking compounds. Typical transport data exhibited T/sub c/'s >87 K, transition widths <1 K, and J/sub c/'s >10/sup 6/ A/cm/sup 2/ (measured inductively at 77 K, 0 T). Microwave surface resistance measurements (36.4 GHz) at temperatures between 20 K and 100 K, made using a copper-cavity end-wall-replacement technique, showed a sharp drop through the transition temperature and yielded values at 77 K that were better than a 20* improvement over copper metal when scaled to 10 GHz. Double-sided coatings have been obtained by sequentially depositing each side of the substrate. Contamination of the backside during growth of the first-side film and of the first-side film during growth of the second-side film has been avoided by coating the susceptor with gold.< <ETX xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">></ETX>
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.