Abstract
Solid solution Ca0.6(La1-xYx)0.2667TiO3 dielectric ceramic systems with various x values were studied, which were prepared using a solid-state reaction method. X-ray diffraction and X-ray spectroscopy analyses showed that the crystal structure of these samples was orthorhombic perovskite. The microstructures with the substitution amount of Y3+ and the dielectric performances of the Ca0.6(La1-xYx)0.2667TiO3 ceramics were also explored. With x = 0.1, the Ca0.6(La0.9Y0.1)0.2667TiO3 ceramic could be sintered at 1350 °C, and the microwave dielectric performance was found to be strongly correlated with the sintering temperature. A maximum Qf value of 23,100 (GHz), dielectric constant (εr) of 111, and temperature coefficient (τf) of 374.6 ppm/°C were achieved for samples sintered at 1350 °C for 4 h. This dielectric ceramic possessed good potential as a τf compensator to obtain a near-zero τf mixture for high-quality substrates for use in wireless communication systems.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.