Abstract
Rapid synthesis of calcium deficient hydroxyapatite (CDHA, Ca(10-x)(HPO4)x(PO4)(6-x)(OH)(2-x)) with Ca/P ratio 1.5 was done by precipitation using calcium nitrate tetra-hydrate and phosphoric acid and subsequently subjecting to microwave irradiation in a domestic microwave oven for 15 min. Transmission electron microscopy analysis shows needle like morphology of CDHA having length 16-39 nm and width 7-16 nm. The synthesized CDHA has the characteristic HPO4(2-) vibration band at 875 cm(-1) in Fourier transform infrared (FT-IR) spectra. The X-ray powder diffraction (XRD) analysis shows a pattern corresponding to stoichiometric hydroxyapatite (HA) with broad peaks suggesting that CDHA particles were nanosized. Fourier transform Raman spectroscopy (FT-Raman) do not indicate any fluorescence band that is characteristic of non-stoichiometric HA. The thermal decomposition of CDHA to beta tricalcium phosphate (beta-TCP) was also studied for the additional confirmation. The nanosized CDHA was found to be stable up to 600 degrees C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Medicine
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.