Abstract
The effect of Cr3+ ions doping on the electromagnetic (EM) properties of polycrystalline U-type hexaferrite samples: Ba4Co2-3xCr2xFe36O60 (0.0≤x≤0.60, in steps of 0.15) have been studied. The X-ray diffraction (XRD) studies confirmed the formation of single U-type hexaferrite phase in all the prepared samples. Le Bail refinement of XRD patterns was used to calculate the lattice parameters ‘a’ and ‘c’. The room temperature M–H studies indicate that the saturation magnetization (Ms) decreases and coercivity (Hc) increases with increasing Cr3+ ions concentration. The complex permittivity (ε*=ε′−iε″) and permeability (μ*=μ′−iμ″) measurement were carried out using vector network analyser (VNA) over 2–18GHz frequency range. The complex permeability (μ*=μ′−μ″) spectra clearly observed the ferromagnetic resonance (FMR) phenomenon in all the prepared samples. The maximum microwave absorption (MWA) of 99.97% (or minimum reflection loss RLmin=−34.90dB) was observed for Ba4Co1.1Cr0.6Fe36O60 sample at 8.2GHz frequency with 1.7mm absorber thickness. The RLmin peak was found to shift towards higher microwave (MW) frequency with increase in Cr3+ ions concentration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.