Microtensile Bond Strength of Resin Cement to a Feldspathic Ceramic

Abstract

The purpose of this study was to evaluate the microtensile bond strength of resin cement to a feldspathic ceramic after treating the surface with (a) hydrofluoric (HF) acid, (b) air abrasion, (c) Er:YAG laser irradiation, (d) Nd:YAG laser irradiation, and (e) HF acid etching after either air abrasion or laser irradiation. It is unknown whether the laser application or its combination with another treatment method can be used as a tool to roughen the surface of a feldspathic ceramic in order to increase the bond strength between the resin cement and ceramic surface. Forty feldspathic ceramic blocks (Ceramco(TM)) were prepared and divided into eight equal groups (n = 5) according to the following surface treatments: no treatment; etching with 9.5% HF acid; air abrasion with 50 μm Al(2)O(3); Er:YAG laser irradiation; Nd:YAG laser irradiation; air abrasion plus acid etching; Er:YAG laser plus acid etching; and Nd:YAG laser plus acid etching. After surface treatment, a silane-coupling agent and resin cement (Panavia F(TM)) were applied to each block. After storing for 24 h at 37°C and thermocycling between 5°C and 55°C for 1000 cycles, the microtensile bond strength of each specimen was measured. The highest bond strength was obtained from HF acid etching. HF acid etching after each laser irradiation significantly increased the bond strength (p < 0.05). However, HF acid etching after air abrasion decreased bond strength when compared to air abrasion alone. HF acid etching is the most effective surface treatment method for a feldspathic ceramic. However, laser irradiation with either the Er:YAG or Nd:YAG laser is not an adequate method for improving the bond strength of Panavia F. The laser application should be combined with HF acid etching.