Abstract
Microstructures and tensile properties of Al-2024 matrix composite containing 10wt% Al4Sr intermetallic have been studied after extrusion process and T6 heat treatment. Microstructural examinations were assessed by the use of optical microscopy, scanning electron microscopy (SEM) and X-ray diffractometry. The results showed that changing the matrix from Al to 2024 alloy reduces the length of primary Al4Sr particles and improves ultimate tensile (UTS) values considerably from 206MPa to 321MPa which is based on the formation of Cu-rich intermetallics. Applying extrusion process and T6 heat treatment was found to be very effective in enhancing tensile properties of Al/2024–10Al4Sr composite. In current research, UTS and elongation values were found to be 381MPa and 13.6%, introducing a tough composite. Moreover, the study of fracture surfaces of the hot-extruded composites specimens revealed that ductile mode of fracture is dominant.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.