Abstract
The aim of this study was to investigate the effects of welding current and welding time on the microstructure and mechanical properties of welding joints. To this end, two dissimilar materials, austenitic stainless steel alloy SUS301L and aluminum alloy 6063-T6, were welded together via intermediate frequency resistance spot welding. A thick, two-layered intermetallic compound layer containing FeAl3 and Fe2Al5 phases was formed at the SUS301L/6063-T6 interface. As the welding current and welding time increased, the nugget diameter increased, the interfacial layer structure became coarser, the thickness of the interfacial intermetallic compound increased, and the tensile shear load of the weld joints had an increased welding tendency in stainless steel/aluminum joints. The nugget diameter reached 5.4 mm, and the maximum tensile shear load reached 1783 N at 7 kA for 200 ms of welding time. The resistance spot welded joint exhibited an interfacial fracture mode in the welded joint. The crack initiated at the interfacial intermetallic compound layer near the aluminum alloy side and spread through the interfacial layer, as well as through the aluminum alloy fusion zone near the interface.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.