Abstract
The present study dealt with the AZ91 alloy subjected to multidirectional forging (MDF) under decreasing temperature conditions with emphasizing on relationship between microstructures and mechanical properties generated by MDF. The obtained results showed that grains of the alloy were gradually refined while the amount of the second phase precipitated along the grain boundaries was increased with increasing the MDF passes and decreasing the MDF temperature. Compared with the as-cast alloy, yield strength, ultimate tensile strength and elongation of the AZ91 alloy after MDF under decreasing temperature conditions were simultaneously increased. As the numbers of MDF passes were gradually increased and the MDF temperature was gradually decreased, the yield strength was gradually decreased, suggesting that texture softening may overwhelm the strengthening due to the grain refinement as well as the homogeneous distribution of precipitates.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call