Microstructures and formation mechanism of W–Cu composite coatings on copper substrate prepared by mechanical alloying method

Abstract

In the present work, high-energy mechanical alloying (MA) method was applied to prepare tungsten–copper composite coatings on pure copper surface using a planetary ball mill. During mechanical alloying process, grains on the surface layer of substrate were refined and the substrate surface was activated as a result of repeated collisions by a large number of flying balls along with powder particles. The repeated ball-to-substrate collisions resulted in the deposition of coatings. The microstructures and elemental and phase composition of mechanically alloyed coatings at different milling durations during mechanical alloying process were studied using scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDS). Microhardness tests were carried out to examine the mechanical properties of the coatings. The results showed that the coatings and the substrates were well bonded, and with the increase of the milling duration, multi-layered coatings with different structures were generated and the coatings became denser. The microhardness tests showed that the maximum microhardness of the coatings reached HV0.1 228, showing a threefold improvement upon the substrate. And the cross-sectional microhardness values of the processed sample changed gradually, which gave a proof for the cushioning and sustaining functions of the multi-layered coatings. A reasonable formation mechanism of coatings on bulk materials with metallic immiscible system by mechanical alloying method was presented.