Microstructure-Fracture Behavior Relationships of Slot-Welded Rail Steels

Abstract

Microstructural analyses of the parent pearlitic and bainitic rail steels were performed, and the results were compared with the microstructure of the welded pearlitic and bainitic steels. An increase in the ASTM grain size number of the heat-affected zone (HAZ) for both pearlitic and bainitic slot welds was observed. The microstructural features that were identified in the weldment of both slot-welded steels were very similar. This was expected since the same welding wire was used to weld both rail steels. The weld consisted of mainly ferrite and had similar grain size. The fusion zones of the welded pearlitic and bainitic rail steels were examined after flexural tests to determine if there were any cracks present due to improper or weak fusion. Examination of the entire fusion zone under high optical magnification revealed no cracks, indicating that a perfect fusion was achieved. The three-point flexural behavior of the parent pearlitic and bainitic steels was evaluated and compared with that of the slot-welded steels. It was found that that the welded pearlitic steel has superior fracture resistance properties when compared to the parent pearlitic steel. The average fracture resistance of the parent pearlitic steel was 79 MPa√m compared to 119 MPa√m for the welded pearlitic steel. The slot-welded bainitic steel, however, showed similar fracture resistance properties to the parent bainitic steel with average values of 121 and 128 MPa√m, respectively. The failure mechanism of the welded and parent pearlitic and bainitic steels was also identified. Microvoid coalescence was observed in both welded rail steel samples. This was manifested by dimpled features, which are associated with ductile failure.