Abstract
AbstractStructure–properties relationship in complex rubber nanocomposites is a key for enlarging the performance window. Herein, halloysite nanotubes (HNTs) are added at variable content to ethylene-propylene diene monomer (EPDM)/nitrile butadiene rubber (NBR) rubber blends compatibilized with maleic anhydride grafted HNTs to evaluate cure characteristics, along with microstructure, and mechanical and swelling behavior. The crosslinking rate increased by HNTs loading, but the scorch time decreased. Moreover, a 45% rise in tensile strength was observed for systems containing 10 wt% HNTs. SEM and TEM micrographs revealed a rough fracture surface with proper dispersion of HNT within EPDM/NBR. The modulus of EPDM/NBR/HNTs nanocomposites is theoretically estimated by modified Kolarik model, demonstrating a good agreement with experimental value. Dynamic mechanical thermal analysis (DMTA) revealed a higher storage modulus up to 2.27 GPa with the introduction of HNTs into EPDM/NBR compound. Correspondingly, lower solvent uptake (decreased by 38%) is reported. Thermogravimetric analysis (TGA) revealed higher thermal stability for highly-loaded systems.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.