Abstract
Abstract The paper presents rezults of microstructure (LM, TEM) investigation and hardness measurments of welded joints in martensitic precipitation hardened stainless steel containing copper, subjected to heat treatment. For the aging temperature up to 540 °C even for the very long times, the microstructure of the welded joints is similar to this one at lower temerature aging. After aging at 620 °C a distinct change of the microstructure was observed. Non-equilibrium solidification conditions of the weld metal, segregation and the diffusion of copper and the elements stablilizing the austenite cause the occurrence of the reverse transformation of the martensite into austenite as fast as just 1 hour at 620 °C. TEM investigations revealed the differences in dispersion of hardening copper precipitates after aging at temperature 620 °C for 1 and 4 hours.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.