<p>A deep cryogenic heat treatment (DCT) was applied to X37CrMoV5 steel, which included soaking at -160°C for 12 and 30 hours followed by tempering at 180°C. Microstructures were compared with those after conventional heat treatment (HT). Microstructures with conspicuous dendritic segregation were observed in all specimens. After HT coarser and finer tempered martensite occurred in depleted and enriched areas of carbon and alloying elements respectively. Coarse molybdenum and vanadium carbides, fine secondary Fe2MoC carbides and retained austenite were identified after HT. Deep freezing resulted in microstructure refinement, transformation of retained austenite into twinned martensite, spinodal decomposition of martensite plates and precipitation of semicoherent h-carbide. The mechanism of h-carbide precipitation was discussed. Wear rate was measured using pin-on-disc test. The best results were obtained after DCT with cryosoaking for 12 hours.</p>
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.