Abstract
The microstructure of the base metal (BM), heat affected zone (HAZ) and the weld metal (WM) of NPP Kozloduy Unit1 Weld 4 after re-irradiation was investigated by scanning and transmission electron microscopy. Structure of tempered upper bainite (enlarged in the HAZ zone) was found in the BM and HAZ. The WM showed a typical fan-like radial structure with a central zone containing fine equiaxial ferrite grains divided by ferrite bands. The structure changed to fully equiaxial at the periphery towards HAZ. Fine elongated particles (up to 50 nm) were distributed irregularly along the grain boundaries in the WM. Regularly distributed structural inhomogeneities (dots) were observed in the grain volume both in WM (with diameter up to 15 nm) and in BM (with diameter up to 50 nm). An annealing experiment was undertaken in order to prove the character of the dots. The 2 h annealing of the thin foils at 560°C showed that the dots of larger size were precipitations, but the character of the smallest ones could not be determined unambiguously. The impact fracture in vacuum of a 1 mm 2 specimen at −120°C developed mainly by transcrystal cleavage and quasi-cleavage.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.