Abstract
Large-sized Fe-based ODS (Oxide Dispersive Strengthen) high-temperature alloy sheets were successfully synthesized by EBPVD (Electron Beam Physical Vapor Deposition) technique. The sheets were about 120μm thick, and having a diameter of 1000mm, whose surface roughness was less than 1μm (Ra<1μm). The microstructures were examined by SEM (Scanning Electron Microscope). The grain size was 1-4μm. When the substrate temperature was 600°C, the sheet had sharp irregular polyhedral grain, and when the substrate temperature was 700°C the sheet had quite regular grains. The morphological orientation angle increased with the distance from the center of the sheet. During the first period of deposition, the sheet was growing in a G-L-S mode, which corresponded with the corn-like microstructure in the cross-section. While during the final period, the sheet changed into a G-S growing mode, which corresponded to the smooth columnar microstructure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.