Abstract
Heat treatment was carried out to the 1420 Al-Li alloy electron beam welding (EBW) joints after welding, and the microstructures of welded joints are analyzed systematically before and after post-weld heat treatment (PWHT). The observation of joint microstructure demonstrates that the grain morphology of weldment changes from equiaxed dendrites in as-welded (AW) condition into equiaxed grains after PWHT, and that the fine strengthening phases precipitate within the grain. The XRD analysis of phase constituent and TEM observation of weldment indicate that the main strengthening phases in 1420 Al-Li alloy weldment are spheroidal δ′(Al3Li), β′(Al3Zr) and rod-like T(Al2MgLi) after PWHT. Furthermore, the δ′ phase precipitate free zone (PFZ) is found along the grain boundary. The scanning observation of joint fracture shows that Al-Li alloy EBW joint presents the characteristic of transgranular ductile fracture in AW condition. After PWHT, the Al-Li alloy welded joint presents the pattern of intergranular fracture. The variation of fracture mode is related to dispersed precipitation of δ′ phase and the formation of PFZ at the grain boundary in weldment after heat treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.