Abstract
Tensile creep tests in the [011] direction have been performed on two specimens of SRR99 at 1173 K under a load of 300 MPa. The microstructure was analysed by transmission electron microscopy investigations after plastic strains of 0.1% and 0.29%. At both strains, the γ′ phase is not sheared by dislocations. Plastic deformation is concentrated in roof matrix channels lying at an angle of 45° to the load axis. Gable matrix channels that contain the load axis are almost free of dislocations. This experimental result was shown to be due to the superposition of coherency and external load stress tensors, leading to different levels of shear stress in the two types of matrix channel. The results obtained at 1173 K are compared with previous results at 1033 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.