Abstract
In this paper, biomedical porous Ti–Nb–Ta–Zr with 40% porosity and 166 ± 21 μm macro-pore size was successfully fabricated by space holder method. The microstructure, Vickers hardness, compressive and electrochemistry behavior were studied. It results that a few second phases exist in β matrix of the porous Ti–Nb–Ta–Zr. Its Young's modulus is 0.8 GPa, close to 0.01–3 GPa for trabecular bone. The total recovery strain ratio and pseudoelastic strain ratio are 8.8% and 2.7%, respectively. It fails mainly by brittle cleavage with the fan-shaped and smooth cleaved facets. Although, local ductile fracture by a few dimples and a small amount of transcrystalline fracture with the cleavage of similarly oriented laths in a colony are observed on the fracture surface. The impedance spectrum of porous Ti–Nb–Ta–Zr has the characteristics of half capacitive arc resistance, showing good corrosion resistance in SBF solution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.