Microstructure, mechanical properties and wear resistance of an Al–Mg–Si alloy produced by equal channel angular pressing

Abstract

Microstructure, mechanical properties and wear resistance in an ultrafine-grained Al–Mg–Si alloy fabricated utilizing a combination of equal channel angular pressing (ECAP) and dynamic aging were investigated in this paper. The results indicated that the grain size of the ECAP alloy was significantly refined, i.e., to ~239 nm after three ECAP passes. Meanwhile, the yield and tensile strength of the ECAPed material reached 340 MPa and 445 MPa, respectively, while maintaining a significant uniform elongation of 14%. Wear resistance results demonstrated that the wear rate, wear depth and width of the ECAPed material decreased in comparison with the solution-treated (SST) and peak-aged (T6) conditions under a load range of 5–25 N. The adhesive wear that occurs in the undeformed specimens at 10 N does not appear in the ECAPed specimen at the same load, indicating that the ECAPed specimen delay the appearance of more serious wear mechanisms under certain loads. The cooperative interaction of high density nano-scale β" precipitates and dislocations resulted in a combination of super-high strength and good work hardening ability which suppressed the extension of cracks between the friction layer and the plastic deformation zone. As a consequence, the combination of ECAP and dynamic aging brings a significant improvement for antifriction performance of the 6061 aluminum alloy.