Abstract
The microstructure evolution, mechanical and corrosion properties of Al–11Si–2Cu–0.8Zn die cast alloy treated with Bi, Sb and Sr additions were investigated. The results of mechanical testing showed that all additions increased impact toughness, ultimate tensile strength, and elongation of the alloy as a result of change in eutectic Si morphology. The analysis of fracture surfaces revealed that with addition of Sr and to lesser extent Bi and Sb, the alloy exhibited a predominantly ductile fracture rather than quasi-cleavage brittle fracture. Moreover, with the additions of Sr, Bi and Sb, the quality index increased to 164.7 MPa, 156.3 MPa and 152.6 MPa respectively from 102 MPa for the base alloy. Polarization corrosion tests conducted in sodium chloride solution showed that the corrosion potential shifted to more negative values with additions of Sb, Bi and Sr, respectively. Corrosion immersion tests also revealed that the element additions have a detrimental effect on the corrosion rate of alloys, due to the increase of boundaries between the Al and eutectic Si phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.