Abstract
Two types of SiC fibers, one is low-oxygen and carbon-rich fiber denoted by 601-4 and the other is low-oxygen and near-stoichiometric Tyranno SA, were irradiated with 450 keV C+ ions at room temperature. The Raman spectra indicate that irradiation induced distortion and amorphization of SiC crystallites in fibers. TEM characterization of Tyranno SA suggests that SiC crystallites undergo a continued fragmentation into smaller crystalline islands and a continued increase of surrounding amorphous structure. The SiC nano-crystallites (<15 nm) in 601-4 fiber are more likely to be amorphized than larger crystallites (∼200 nm) in Tyranno SA. The hardness and modulus of 601-4 continuously decreases with increasing fluence, while that of Tyranno SA first increases and then decreases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.