Abstract
RF MEMS (Radio Frequency Micro Electro Mechanical System) switches are promising devices but their gold-on-gold contacts, assimilated for this study to a sphere/plane contact, represent a major reliability issue. A first step toward understanding failure mechanisms is to investigate the contact metal microstructure evolution under static and cyclic loading. After static and cyclic loading of sputtered gold thin films under spherical indentation, high-resolution Electron Back Scatter Diffraction (EBSD) is used to investigate the contact area. Grain rotation against {111} fiber texture of 1-μm-thick sputtered gold thin film is a signature of plastic deformation. Grain rotation is observed above 1.6 mN under static loading using a spherical diamond indenter with 50-μm tip radius. The heterogeneity in grain rotation observed corresponds to a greater plastic deformation in the middle of the indent than at the edge. A 30° grain rotation due to cyclic work hardening is observed for a half-million mechanical cycles under 300 μN load using a spherical gold tip (20 μm radius). The same test in hot switching mode induces a grain growth in the contact area. Therefore, thermal effects occurring during hot switching are underlined.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.