Microstructure Evolution In Metal Nanostructures Under Extreme Conditions Of Temperature And Strain Rate

Abstract

This paper explores a fundamental connection between ductility and domain size in metallic solids under extreme conditions of cryogenic temperatures and strain rates (10 8 s –1 ). A series of novel experiments, backed by multiscale modelling and transmission electron microscopy (TEM) analysis, are presented that involve loading of TEM-ready single crystal nanopillar samples of Cu of varying lengths (50 nm to 1 mm) and aspect ratios (50 nm to 100 nm in diameter) by laser-generated stress waves of sub-nanosecond rise times, under extreme conditions of strain rate (>10 8 s –1 ) and temperature (100K). The nucleation stress for Shockley partials, which can be taken as a proxy for the onset of ductile deformation, was measured to be only 1 GPa. This is an order of magnitude lower than the previously measured values of 35 GPain bulk geometries. TEM observations show remarkable ability of the material to re-arrange itself through motion of dislocations to form subgrain boundaries within a very short duration of only few nanoseconds.