Abstract
Carbon nanotubes reinforced pure aluminum (CNT/Al) composites were fabricated by combined ball milling and powder metallurgy (PM) techniques. The distribution of CNTs, the evolution of the average Al grain size of the powder mixtures and as-prepared composite bulks were investigated, and the mechanical properties of the composites were also tested. With increasing ball milling time, the entangled CNTs were broken, gradually achieving a uniform dispersion within the Al matrix. The microstructure became denser and the Al grains in the powder mixture and extruded composites got significantly refined. Some small-sized Al4C3 needles along the Al grain boundaries were observed using transmission electron microscopy (TEM). The in-situ formed Al4C3 rods have an orientation relation with the Al matrix as Al4C3 [110]//Al [1¯12], which strongly improved the Al-CNT interface bonding. The yield and the ultimate tensile strength of the composites significantly increased, when the ball milling time increased from 2 to 12h, finally reaching about 210±4.2MPa and 253±3.7MPa, respectively, for the composite milled for 12h. The enhancement of mechanical properties mainly stems from the uniform distribution of CNTs, the grain refinement of the Al matrix and the in-situ formed Al4C3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.