Abstract
A two-step treatment was proposed to strengthen the surface mechanical performance of 2024 Al alloys. Nano-scale Cr film was firstly deposited by using magnetron sputtering, then Al alloys deposited with Cr film were plasma nitrided at different temperatures (400-480 °C). Results showed that nitriding treatment transformed the Cr film to Cr(N) and CrN phase. With increasing temperature, the nitride surfaces became denser and the nitrogen content (at. %) increased from 17% to 40% at 480 °C. Low temperature nitriding obtained only single Cr-N layer on the surface of Al substrate. High temperature nitriding stimulated surface Cr-N reaction and inner Cr-Al reaction simultaneously to generate multilayer coatings consisting of outmost Cr-N layer and inner Al-Cr intermetallic layers (Al4Cr and Al18Cr2Mg3). The surface hardness of as-prepared coatings reached the maximum value of 9.21 GPa, which significantly enhanced the Al alloy surface (1.57 GPa). The friction coefficient of Al alloy (0.72) was decreased to 0.51 for samples with multilayer coatings. The multilayer coatings showed a mixture wear mechanism of adhesive wear and abrasive wear, accompanied by oxidative wear.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.