Abstract
The microstructure evolution of 2196 Al-Li alloy during aging was investigated by microhardness test, transmission electron microscope (TEM) analysis and in situ resistivity measurement. The results showed that the resistivity of the 2196 Al-Li alloy during aging rapidly decreased during the first few hours, and then gradually increased after reaching the minimum value, which is temperature−dependent. The microstructure of the alloy was dominated by the δ′ phase after aging at 160 °C for 2 h while the T1 phase could hardly be seen until it had been aged for 16 h. As the aging time went on, significant ripening appeared for the δ′ phase while typical growth could be observed for the T1 phase. The increase in the resistivity of the 2196 Al-Li alloy during aging was attributed to the stronger electron scattering capacity of the T1 precipitation and the coupling effect between the T1 and δ′ phases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.